| COUNTRY | SPECIFICATION | DESIGNATION | 150 | 180 | 200 | 220 | 250 | 260 | 300 | 350 |
|---|---|---|---|---|---|---|---|---|---|---|
| India | IS 210 1978 | FG | 150 | -- | 200 | -- | 250 | -- | 300 | 350 |
| United Kingdom | BS 1452 1990 | Grade | 150 | 180 | 200 | 220 | 250 | -- | 300 | 350 |
| USA | ANS/ASTM A48-83 | CLASS | 20A | 25A | 30A | -- | 35A | 40A | 45A | 50A |
| DIN | DIN EN 1561 | EN-GJL | 150 | -- | 200 | -- | 250 | -- | 300 | 350 |
| Germany | DIN 1691 1985 | GG | 15 | -- | 20 | -- | 25 | -- | 30 | 35 |
| France | NFA 32-101-1987 | FGL | 150 | -- | 200 | -- | 250 | -- | 300 | 350 |
| Italy | UNI 5007 1969 | G | 15 | -- | 20 | -- | 25 | -- | 30 | 35 |
| Japan | JIS G5501 1981 | FC | 150 | -- | 200 | -- | 250 | -- | 300 | 250 |
| Russia | GOST 1412 1979 | Sch | 15 | 18 | 20 | -- | 25 | -- | 30 | 35 |
| International | ISO 185-1988 | Grade | 150 | -- | 200 | -- | 250 | -- | 300 | 350 |
| CLASS | 2 | -- | 3 | -- | 4 | -- | 5 | 6 | ||
| Tensile strength MPA | 150 MIN | 207 Min | 242 Min | 350 Min | 350 Min | |||||
| Hardness range BHN | 136-167 | 159-194 | 180-222 | 202-247 | 227-278 | |||||
| Total carbon % | 3.4-3.6 | 3.2-3.5 | 3.15-3.30 | 2.9-3.1 | 3.1 max | |||||
| silicon % | 2.2-2.5 | 2.0-2.5 | 1.6-1.9 | 1.8-2.0 | 1.4-1.6 | |||||
| Mangenese % | 0.5-0.7 | 0.6-0.8 | 0.6-0.8 | 0.7-0.9 | 0.7-0.9 | |||||
| Sulphur % | 0.15 | 0.15 | 0.12 max | 0.10 max | 0.10 max | |||||
| Phosphorous % | 0.9-1.2 | 0.4 max | 0.3 max | 0.10 max | 0.10 max | |||||
| Molybdenum % | -- | -- | -- | -- | 0.3-0.5 | |||||
| Cu or Ni % | -- | -- | -- | 0.3-0.5 | 1.0-1.5 | |||||
NOTE: The above standards for ordering reference only the customer can specify any special requirement. All specifications are subject to change without prior notice.
| Country | Specification | Designation | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| India | IS 1083 | SG | 400/12 | 400/18 | 400/18 LT | 500/7 | 600/3 | 700/2 | ||
| United Kingdom | BS2789:1985 | 420/12 | 400/18 | 400/18 | 500/7 | 600/3 | 700/2 | |||
| USA | ASTM A536 | Grade | 65-45-12 | 60-40-18 | 60-40-18 | 80-55-06 | 80-60-03 | 100-70-03 | ||
| DIN | DIN EN 1563 | EN-GJS | 400-12 | 400-18(RT) | 400-18(LT) | 500-7 | 600-3 | 700-2 | ||
| Germany | Din 1693-1973 | GGG | 400-12 | 400-18 | -- | 500-7 | 600-3 | 700-2 | ||
| France | NF A 32-201:1976 | FGS | 400/12 | 370/17 | 370/17 | 500/7 | 600/3 | 700/2 | ||
| Italy | UNI 4544:1979 | GS | 400/12 | 370/17 | 370/17 | 500/7 | 600/3 | 700/2 | ||
| Japan | JIS G5502:1982 | FCD | (40)392/12 | (37)363/17 | (37)363/17 | (50)490/7 | (60)588/3 | (70)686/2 | ||
| International | ISO 1083:1976 | 400/12 | 370/17 | 370/17 | 500/7 | 600/3 | 700/2 | |||
| Tensile Strength Mpa | 448 MIN | 414 MIN | 414 MIN | 552 MIN | 600 MIN | 689 MIN | ||||
| Yield Strength Mpa | 310 MIN | 276 MIN | 276 MIN | 379 MIN | 370 MIN | 483 MIN | ||||
| Elongation % | 12% | 18% | 18% | 7% | 3% | 2% | ||||
| Impact Joules | - | 14 J AVERAGE | 12 J AVERAGE | - | - | - | ||||
| Hardness range BHN | 156-217 | 149-187 | 149-187 | 187-255 | 192-269 | 241-302 | ||||
| Heat Treatment Requirement | N/A | ANNEALING | ANNEALING | N/A | N/A | N/A | ||||
| Structure-Matrix | 80% FERRITE | 95% FERRITE | 95% FERRITE | 50% FERRITE | 60% FERRITE | 80% PEARLITE | ||||
| Total carbon % | 3.30-3.80 | 3.30-3.80 | 3.30-3.80 | 3.30-3.80 | 3.30-3.80 | 3.20-3.80 | ||||
| Silicon % | 1.80-2.80 | 1.80-2.80 | 1.80-2.80 | 1.80-2.80 | 1.80-2.80 | 1.80-2.80 | ||||
| Mangenese % | 0-0.40 | 0-0.40 | 0-0.40 | 0-0.60 | 0-0.80 | 0-0.80 | ||||
| Phosphorous % | 0-0.06 | 0-0.06 | 0-0.06 | 0-0.06 | 0-0.06 | 0-0.06 | ||||
| Sulphur % | 0-0.03 | 0-0.03 | 0-0.03 | 0-0.03 | 0-0.03 | 0-0.03 | ||||
| Magnesium% | 0.025-0.060 | 0.025-0.060 | 0.025-0.060 | 0.025-0.060 | 0.025-0.060 | 0.025-0.060 | ||||
| Copper% | - | - | - | 0.50-1.00 | 0.50-1.00 | 0.50-1.00 | ||||
| Nickel% | - | - | - | - | 0.04-0.1 | 0.04-0.1 | ||||
NOTE: The above standards for ordering reference only the customer can specify any special requirement. All specifications are subject to change without prior notice.
Lead Free
(Where Lead is an impurity)
| Class | Country | Specification | Cu | Sn | Pb | Zn | Fe | Ni | Al | Mn | Sb | Si | S | As | P | UTS (ksi) | YS (ksi) | Elong % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Gunmetal | USA | C 83600 | 84-86.0 | 4-6.0 | 4-6.0 | 4-6.0 | 0.3 max | 1 max | 0.005 max | - | 0.25 max | 0.005 max | 0.08 max | - | 0.05 max | 30 | 14 | 20 |
| USA | C 92410 | Bal | 6-8.0 | 2.5-3.5 | 1.5-3.0 | 0.2 max | 0.2 max | 0.005 max | 0.05 max | 0.25 max | 0.005 max | - | - | |||||
| USA | C 93200 | 81-85.0 | 6.3-7.5 | 6-8.0 | 1-4.0 | 0.2 max | 1 max | 0.005 max | - | 0.35 max | 0.005 max | 0.08 max | - | 0.15 max | 30 | 14 | 15 | |
| United Kingdom | LG2 | Bal | 4-6.0 | 4-6.0 | 4.5-6.0 | 0.25 max | 2 max | 0.01 max | - | 0.5 max | 0.02 max | 0.1 max | - | 0.02 max | Similar to C83600 ASTM | |||
| United Kingdom | LG4 | Bal | 6-8.0 | 2.7-3.5 | 1.7-3.2 | 0.2 max | 2 max | 0.01 max | - | 0.4 max | 0.01 max | 0.1 max | - | 0.02 max | 45 | 20.319303338171 | 40 | |
| United Kingdom | Rg7 | 81-84.5 | 6.2-8.0 | 5.2-8 | 2.3-5.0 | 0.2 max | 2 max | 0.01 max | - | 0.3 max | 0.01 max | 0.08 max | - | 0.03 max | Similar to C93200 ASTM | |||
| Germany | GB-Cu Sn5 Zn Pb | 83.5-85.5 | 4.3-6.0 | 4-6.0 | 4.5-6.5 | 0.2 max | 2.3 max | 0.01 max | 0.1 max | 0.25 max | 0.01 max | 0.06 max | 0.1 max | 0.03 max | Similar to C83600 ASTM | |||
| Germany | GB-Cu Sn6 Zn Ni | 83.5-87.0 | 5.8-7.0 | 2.8-4.0 | 1.8-3.0 | 0.2 max | 1.5-2.3 | 0.01 max | 0.1 max | 0.2 max | 0.01 max | 0.06 max | 0.1 max | 0.03 max | ||||
| Germany | GB-CU Sn7 Zn Pb | 81-84.5 | 6.3-8.0 | 5.3-7.0 | 3.3-5.0 | 0.2 max | 1.8 max | 0.01 max | 0.1 max | 0.25 max | 0.01 max | 0.06 max | 0.1 max | 0.03 max | Similar to C93200 ASTM | |||
| Japan | BCIn6 | 83-87.0 | 4-6.0 | 4-6.0 | 4-6.0 | 0.3 max | 0.8 max | 0.005 max | - | 0.2 max | 0.005 max | - | - | 0.03 max | Similar to C83600 ASTM | |||
| Japan | BCIn7 | 86-65.0 | 5-7.0 | 1-3.0 | 3-5.0 | 0.2 max | 0.8 max | 0.005 max | - | 0.2 max | 0.005 max | - | - | 0.03 max | ||||
| Italy | G-Cu Sn 5 Zn5 Pb5 | Bal | 4-6.0 | 4-6.0 | 4-6.0 | 0.3 max | 2 max | - | 0.1 max | 0.4 max | 0.1 max | - | 0.05 max | Similar to C83600 ASTM | ||||
| India | LTB-2 | Bal | 4-6.0 | 4-6.0 | 4.5-6.0 | 0.35 max | 2 max | 0.01 max | - | 0.4 max | 0.02 max | - | - | - | Similar to C83600 ASTM | |||
| Tin Bronze | USA | C 90500 | 86-89.0 | 9-11.0 | 0.3 max | 1-3.0 | 0.2 max | 1 max | 0.005 max | - | 0.2 max | 0.005 max | 0.05 max | - | 0.05 max | 40 | 18 | 20 |
| United Kingdom | G1 | Bal | 9.7-10.5 | 1.50 | 1.75-2.75 | 0.15 max | 1 max | 0.01 max | - | 0.02 max | 0.1 max | - | 0.02 max | Similar to C90500 ASTM | ||||
| Germany | GB-Cu Sn10 Zn | 86-88.5 | 9.2-11.0 | 1.30 | 1-3.0 | 0.2 max | 1.8 max | 0.01 max | 0.1 max | 0.25 max | 0.01 max | 0.06 max | 0.1 max | 0.03 max | Similar to C90500 ASTM | |||
| Japan | BCIn3 | 86.5-89.5 | 9-11.0 | 1.00 | 1-3.0 | 0.2 max | 0.8 max | 0.005 max | - | 0.2 max | 0.005 max | - | - | 0.03 max | Similar to C90500 ASTM | |||
| Phsophor Bronze | USA | C 90800 | 85-89.0 | 11-13.0 | 0.25 max | 0.25 max | 0.15 max | 0.5 max | 0.005 max | - | 0.2 max | 0.005 max | 0.05 max | - | 0.3 max | 35 | 17 | 10 |
| United Kingdom | PB2 | Bal | 11.2-13.0 | 0.5 max | 0.3 max | 0.1 max | 0.5 max | 0.01 max | - | 0.02 max | 0.1 max | - | 0.25-0.6 | 45 | 25 | 5 | ||
| Japan | PBCIn2 | 87-91.0 | 9-12.0 | 0.3 max | 0.3 max | 0.2 max | 0.5 max | 0.005 max | - | 0.05 max | 0.005 max | - | 0.1 max | Similar to BS1400 PB2 | ||||
| Lead Bronze | USA | C 93700 | 78-82.0 | 9-11.0 | 8-11.0 | 0.8 max | 0.7 max | 0.5 max | 0.005 max | - | 0.5 max | 0.005 max | 0.08 max | - | 0.1 max | 30 | 16 | 12 |
| United Kingdom | LB2 | Bal | 9.2-11.0 | 9-10.5 | 1 max | 0.15 max | 2 max | 0.01 max | 0.2 max | 0.5 max | 0.02 max | 0.1 max | - | 0.05 max | Similar to C93700 ASTM | |||
| Germany | GB-Cu Pb10 Sn | 78-81.0 | 9.3-11.0 | 8.5-10.5 | 0.8 max | 0.15 max | 1.3 max | 0.01 max | 0.1 max | 0.3 max | 0.01 max | 0.08 max | 0.1 max | 0.03 max | Similar to C93700 ASTM | |||
| Japan | LBCIn3 | 77-81.0 | 9-11.0 | 9-11.0 | 1 max | 0.2 max | 1 max | 0.005 max | - | 0.5 max | 0.005 max | - | - | 0.05 max | Similar to C93700 ASTM | |||
| Aluminium Bronze | USA | C 95200 | Min 86 | - | - | 2.5-4.0 | 8.5-9.5 | - | - | - | - | - | - | 65 | 25 | 20 | ||
| USA | C 95800 | Min 79 | - | 0.03 max | - | 3.5-4.5 | 4-5.0 | 8.5-9.5 | 0.8-1.5 | - | 0.01 max | - | - | - | 85 | 35 | 15 | |
| USA | C 95500 | Min 78 | - | - | - | 3-5.0 | 3-5.5 | 10-11.5 | 3.5 max | - | - | - | - | - | 90 | 40 | 6 | |
| USA | C 95900 | Bal | - | - | - | 3-5.0 | 0.5 max | 12-13.5 | 1.5 max | - | - | - | - | - | ||||
| United Kingdom | AB1 | Bal | 0.1 max | 0.03 max | 0.5 max | 1.5-3.5 | 1 max | 8.7-10.5 | 1 max | 0.05 max | 0.2 max | - | - | - | 68 | 26 | 20 | |
| United Kingdom | AB2 | Bal | 0.1 max | 0.03 max | 0.5 max | 4-5.5 | 4-5.5 | 8.8-10.0 | 3 max | 0.05 max | 0.1 max | - | - | - | 93 | 36 | 13 | |
| Germany | GB-Cu Al10 Fe | 83-89.0 | 0.2 max | 0.1 max | 0.4 max | 2-3.8 | 2.7 max | 8.7-10.7 | 0.8 max | - | 0.1 max | 0.04 max | - | - | Similar to C95200 ASTM | |||
| Germany | GB-Cu Al10 Ni | 76-80.5 | 0.1 max | 0.03 max | 0.2 max | 3.5-5.3 | 4.5-6.3 | 9-10.6 | 2.3 max | - | 0.07 max | 0.04 max | - | - | Similar to C95800 ASTM | |||
| Japan | AIBCIn1 | 85.00 | 0.1 max | 0.1 max | 0.5 max | 1-4.0 | 0.1-1.0 | 8-10.0 | 0.1-1.0 | - | - | - | - | - | Similar to C95200 ASTM | |||
| Japan | AlBCIn4 | 71.00 | 0.1 max | 0.1 max | 0.5 max | 2-5.0 | 1-4.0 | 6-9.5 | 7-15.0 | - | - | - | - | - | Similar to C95800 ASTM | |||
| Manganese Bronze | USA | C 86300 | 60-66.0 | 0.2 max | 0.2 max | 22-28.0 | 2-4.0 | 1 max | 5-7.5 | 2.5-5.0 | - | - | - | - | - | 110 | 60 | 12 |
| United Kingdom | HTB3 | Min 55 | 0.2 max | 0.2 max | Bal | 1.5-3.25 | 1 max | 3-6.0 | 1.5-4.0 | - | 0.1 max | - | - | - | 107 | 58 | 14 | |
| Germany | GB-Cu Zn 25 Al5 | 60-66.0 | 0.05 max | 0.1 max | Bal | 3.5-4.5 | 2.7 max | 4-6.5 | 3-5 | 0.03 max | 0.05 max | - | 0.08 max | 0.02 max | Similar to C86300 ASTM | |||
| Japan | HBsCIn4 | 60-65.0 | 0.2 max | 0.2 max | Bal | 2-4.0 | 0.5 max | 5-7.5 | 2.5-5.0 | - | 0.1 max | - | - | - | Similar to C86300 ASTM | |||
NOTE: The above standards for ordering reference only the customer can specify any special requirement. All specifications are subject to change without prior notice.
| COUNTRY | CF8/SS304 | CF8M/SS316 | WCA | WCB | WCC | LCC | LCB | A487 4C | A487 4D |
|---|---|---|---|---|---|---|---|---|---|
| India | IS 7806 | IS 7806 | IS 2856 : 1999 | IS 2856 : 1999 | IS 2856 : 1999 | IS 1030 : 1998 | - | - | - |
| GRADE 3 | GRADE 5 | GRADE 1 | GRADE 2 | GRADE 3 | 280-520W | - | - | - | |
| USA | ASTM A351/A 351M-06 | ASTM A351/A 351M-06 | ASTM A216/A 216M-04 | ASTM A216/A 216M-04 | ASTM A216/A 216M-04 | ASTM A352/A 352M-06 | ASTM A352/A 352M-06 | ASTM A487 | ASTM A487 |
| CF8 | CF8M | WCA | WCB | WCC | LCC | LCB | Grade 4 Class C | Grade 4 Class D | |
| Germany | DIN 1.4308 | DIN 1.4408 | - | - | - | - | - | - | - |
| Japan | JIS G5121 | G5121 | G5151 | G5151 | - | - | - | - | - |
| SCS13A | SCS14A | SCPH1 | SCPH2 | - | - | - | - | - | |
| International | J92600 | J92900 | UNS J02502 | UNS J03002 | UNS J02503 | UNS J02505 | UNS J03003 | - | UNS J13047 |
| - | - | - | - | - | - | - | - | - | |
| Hardness range BHN | 145-165 | 145-165 | 124 - 176 | 145 - 197 | 145 - 197 | 145 to 197 | 135 - 186 | 187 to 237 | 197 to 237 |
| Tensile Strength,min(Mpa) | 485 | 485 | 415 - 585 | 485 - 655 | 485 to 655 | 485-655 | 450 - 620 | 620 | 690 |
| Yield Strength,min(Mpa) | 205 | 205 | 205 | 250 | 275 | 275 | 240 | 415 | 517 |
| Elongation in 2in,% | 35 | 30 | 24 | 22 | 22 | 22 | 24 | 18 | 17 |
| Reduction of Area,min % | - | - | 35 | 35 | 35 | 35 | 35 | 35 | 35 |
| Energy value Joules impact | - | - | - | - | - | 20 | 14 | 20 | 20 |
| Testing Temperature | - | - | - | - | - | - 46°C | - 46°C | - 46°C | - 46°C |
| Carbon % | 0.08 Max | 0.08 Max | 0.25 Max | 0.3 Max | 0.25 Max | 0.25 Max | 0.30Max | 0.30Max | 0.30Max |
| Silicon % | 2.0 Max | 1.5 Max | 0.60 Max | 0.6 Max | 0.6 Max | 0.6 Max | 0.60 Max | 0.80 Max | 0.80 Max |
| Mangenese % | 1.5 Max | 1.5 Max | 0.70 Max | 1.0 Max | 1.20 Max | 1.20 Max | 1.00Max | 1.00Max | 1.00Max |
| Sulphur % | 0.04 Max | 0.04 Max | 0.045 Max | 0.045 Max | 0.045 Max | 0.045 Max | 0.045 Max | 0.04 Max | 0.04 Max |
| Phosphorous % | 0.04 Max | 0.04 Max | 0.04 Max | 0.04 Max | 0.04 Max | 0.04 Max | 0.04 Max | 0.04 Max | 0.04 Max |
| Copper % | 0 | 0 | 0.30 Max | 0.30 Max | 0.30 Max | 0.30 Max | 0.30 Max | 0.50 Max | 0.50 Max |
| Nickel % | 8.0-11.0 | 9.0-12.0 | 0.50 Max | 0.50 Max | 0.50 Max | 0.50 Max | 0.50 Max | 0.40 -0.80 | 0.40 -0.80 |
| Chromium % | 18.0-21.0 | 18.0-21.0 | 0.50 Max | 0.50 Max | 0.50 Max | 0.50 Max | 0.50 Max | 0.40 -0.80 | 0.40 -0.80 |
| Molybdenum % | 0.50 Max | 2.0-3.0 | 0.20 Max | 0.20 Max | 0.20 Max | 0.20 Max | 0.20 Max | 0.15 - 0.35 | 0.15 - 0.35 |
| Vanadium % | - | - | 0.03 Max | 0.03 Max | 0.03 Max | 0.03 Max | 0.03 Max | 0.03 Max | 0.03 Max |
| Total of these specified residual elements, max | - | - | 1 | 1 | 1 | 1 | 1 | 0.6 | 0.6 |
NOTE: The above standards for ordering reference only the customer can specify any special requirement. All specifications are subject to change without prior notice.
The Allied Founders Pvt. Ltd. is an ISO 9001:2015, 14001:2015 & 45001:2018 certified company producing high quality industrial castings. Manufacturers and exporters of Cast iron, Ductile iron precision machined components and assemblies to original equipment manufacturers (OEM’S) throughout the world. Our export share is 95% of our total production to several countries.
N-3, Industrial Estate, Udyambag,
Belgaum, Karnataka, India – 590 008
Phone : +91-831-2441057
Plot No. 4/2I, Ganeshbag, Sulge Village
Vengurla Road, Belgaum Karnataka, India – 591 108 Phone : +91-831-2441812
321, Courtland Ave, Vaughan,
ON, L4K5B5, Canada